An experimental study on matrix crack induced delamination in composite laminates

Matrix crack induced delamination is one of the predominant failure mechanisms in laminated composites under off-axis loading. However, there exist a reduced number of experimental studies on the literature specifically devoted to this failure mechanism. In this work, an experimental campaign focused on the occurrence of matrix cracking and delamination induced by matrix crack is presented. Five different carbon-epoxy lay-ups have been tested under tensile load, leading to different damage evolutions. The experimental data has been compared with a failure criterion recently developed by the authors. A good agreement between the experimental data and the predictions of the failure criterion has been obtained

This work was funded by AIRBUS under project iComp – the integrated method for the structural design of Composite components. The authors gratefully acknowledge the support provided by Airbus – Germany, along with the support of the Spanish government through DG-CICYT under Contract DPI2012-34465 and MAT2012-37552-C03-03

Elsevier

Manager: Ministerio de Economía y Competitividad (Espanya)
Author: Zubillaga Eceiza, Lierni
Turon Travesa, Albert
Renart Canalias, Jordi
Costa i Balanzat, Josep
Linde, Peter
Abstract: Matrix crack induced delamination is one of the predominant failure mechanisms in laminated composites under off-axis loading. However, there exist a reduced number of experimental studies on the literature specifically devoted to this failure mechanism. In this work, an experimental campaign focused on the occurrence of matrix cracking and delamination induced by matrix crack is presented. Five different carbon-epoxy lay-ups have been tested under tensile load, leading to different damage evolutions. The experimental data has been compared with a failure criterion recently developed by the authors. A good agreement between the experimental data and the predictions of the failure criterion has been obtained
This work was funded by AIRBUS under project iComp – the integrated method for the structural design of Composite components. The authors gratefully acknowledge the support provided by Airbus – Germany, along with the support of the Spanish government through DG-CICYT under Contract DPI2012-34465 and MAT2012-37552-C03-03
Document access: http://hdl.handle.net/2072/296119
Language: eng
Publisher: Elsevier
Rights: Tots els drets reservats
Subject: Materials compostos -- Deslaminatge
Composite materials -- Delamination
Materials laminats
Laminated materials
Assaigs de materials
Materials -- Testing
Materials compostos -- Mètodes de simulació
Composite materials -- Simulation methods
Title: An experimental study on matrix crack induced delamination in composite laminates
Type: info:eu-repo/semantics/article
Repository: Recercat

Subjects

Authors


Warning: Unknown: write failed: No space left on device (28) in Unknown on line 0

Warning: Unknown: Failed to write session data (files). Please verify that the current setting of session.save_path is correct (/var/lib/php5) in Unknown on line 0