| Thermal and field-induced martensite-austenite transition was studied in melt spun Ni50.3Mn35.3Sn14.4 ribbons. Its distinct highly ordered columnarlike microstructure normal to ribbon plane allows the direct observation of critical fields at which field-induced and highly hysteretic reverse transformation starts (H=17kOe at 240K), and easy magnetization direction for austenite and martensite phases with respect to the rolling direction. Single phase L21 bcc austenite with TC of 313K transforms into a 7M orthorhombic martensite with thermal hysteresis of 21K and transformation temperatures of MS=226K, Mf=218K, AS=237K, and Af=244K | |
| http://hdl.handle.net/2072/320463 | |
| eng | |
| American Institute of Physics | |
| Tots els drets reservats | |
|
Aliatges
Alloys Microestructura Microstructure Materials ferromagnètics Ferromagnetic materials Transformacions martensítiques Martensitic transformations |
|
| Thermal and magnetic field-induced martensite-austenite transition in Ni50.3Mn35.3Sn14.4 ribbons | |